QA Cwestiynau Cwsmer Diweddar

Ar ôl cyfnod o ddidoli, fe wnaethom unwaith eto gasglu rhywfaint o adborth gan gwsmeriaid a gwneud erthygl i bawb ei darllen.

C1: Pam fod eich zirconia yn wyrdd ar ôl sintro?

A1:It is because your finance has been polluted, different types of zirconia have different subsidiary substances during production. when sintering the substance will get rid of zirconia and come to the heart of finance, it made the heart of finance was polluted because the substance doesn't get rid of completely.

Pls, sinter the finance empty immediately to help the substance get rid of completely. Each time sintering the heating elements will have new crystalline film. It is better to change the sintering tray and beads as well.

Awgrymiadau i osgoi llygredd:

1, Peidiwch â sinter gwahanol fathau o zirconia yn barhaus.

Er enghraifft, heddiw sintering blociau gwyn, os yfory mae angen blociau sinter cyn cysgodol, dylech sintering y cyllid yn wag ar ôl blociau gwyn yna sinter cyn cysgodol.

2, Dylai'r holl goronau blociau gwyn fod yn sychu 200 gradd 30 munud cyn sintro

C2: Beth yw'r gwahaniaeth rhwng SHT Multilayer a 3D-Plus Multilayer?

A2: Mae SHT yn raddiant lliw. Cryfder yw 1200MPA a 45 y cant tryleuedd.

Mae 3D{1}}Plus yn raddiant lliw a chryfder. Cryfder o 600MPA i 900MPA, tryleuedd o 43 y cant i 49 y cant.

Yn y cyfamser, rydym yn profi E-Plus 3D newydd, gall Cryfder fod yn Uchafswm o 1100 a thryloywder o 47 y cant i 49 y cant .

C3: Pontine torri asgwrn ar ôl gwydro?

A3: Mae dau bosibilrwydd ar gyfer y broblem hon:

1. The upper gingival porcelain requires repeated enamels, and the burned bridge undergoes multiple heating and cooling. Pulling and cracking are caused by the too fast cooling rate.
Suggestions: Lower the cooling rate and reduce the number of times porcelain loading

Porcelain furnace cooling program should be set a little slower, porcelain furnace cooling too fast will cause thermal stress, thermal shock, ceramics are most afraid of rapid cooling and heating, porcelain furnace cooling down a little bit, the lower temperature limit is set a little lower

This needs to be paid attention to in the porcelain furnace, the mouthful of rapid cold causes thermal stress cracking
Generally, the teeth in the porcelain furnace come out at 700 degree  and come into contact with the air, and the teeth at 700 degree  encounter the cold air at 25 degree , which causes cracking.
Easiest to break from the missing position, because the missing position is solid, accumulates more heat, and dissipates slowly

2. When the porcelain is cut, the teeth are cut vertically with fine slices. (In the past, metal teeth and porcelain teeth were cut in this way, so technicians are used to it).

Suggestion: When the car porcelain is cut between the teeth, it should be cut sideways in the direction of the teeth. However, this possibility is generally small.